We report an optimized chemical vapor transport method to grow single crystals of (Mn1−xNix)2P2S6 where x = 0, 0.3, 0.5, 0.7, and 1. Single crystals up to 4 mm × 3 mm × 200 μm were obtained by this method. As-grown crystals are characterized by means of scanning electron microscopy and powder X-ray diffraction measurements. The structural characterization shows that all crystals crystallize in monoclinic symmetry with the space group C2/m (No. 12). We have further investigated the magnetic properties of this series of single crystals. The magnetic measurements of the all as-grown single crystals show long-range antiferromagnetic order along all principal crystallographic axes. Overall, the Néel temperature TN is non-monotonous; with increasing Ni2+ doping, the temperature of the antiferromagnetic phase transition first decreases from 80 K for pristine Mn2P2S6 (x = 0) up to x = 0.5 and then increases again to 155 K for pure Ni2P2S6 (x = 1). The magnetic anisotropy switches from out-of-plane to in-plane as a function of composition in (Mn1−xNix)2P2S6 series. Transport studies under hydrostatic pressure on the parent compound Mn2P2S6 evidence an insulator-metal transition at an applied critical pressure of ~22 GPa. 

Tremendous progress in the development of single molecule magnets (SMMs) raises the question of their device integration. On this route, understanding the properties of low‐dimensional assemblies of SMMs, in particular in contact with electrodes, is a necessary but difficult step. Here, it is shown that fullerene SMM self‐assembled on metal substrate from solution retains magnetic hysteresis up to 10 K. Fullerene‐SMM DySc₂N@C₈₀and Dy₂ScN@C₈₀are derivatized to introduce a thioacetate group, which is used to graft SMMs on gold. Magnetic properties of grafted SMMs are studied by X‐ray magnetic circular dichroism and compared to the films of nonderivatized fullerenes prepared by sublimation. In self‐assembled films, the magnetic moments of the Dy ions are preferentially aligned parallel to the surface, which is different from the disordered orientation of endohedral clusters in nonfunctionalized fullerenes. Whereas chemical derivatization reduces the blocking temperature of magnetization and narrows the hysteresis of Dy₂ScN@C₈₀, for DySc₂N@C₈₀equally broad hysteresis is observed as in the fullerene multilayer. Magnetic bistability in the DySc₂N@C₈₀grafted on gold is sustained up to 10 K. This study demonstrates that self‐assembly of fullerene‐SMM derivatives offers a facile solution‐based procedure for the preparation of functional magnetic sub‐monolayers with excellent SMM performance.